Aluminum Alloy Coil for Body Stock A3104 Temper H19
Aluminum Can Body Stock technical specification
| Alloy | Temper | Thickness and tolerance | Width and tolerance |
| 3104 | H19 | 0.279±0.005mm | 1491.79-0/+1.5mm |
1. Requirement
1.1 Alloy. Temper. Dimension tolerance
1.2 Chemical composition
| Alloy | Chemical composition (not more than) |
| Fe | Si | Cu | Mn | Mg | Ti | Zn | Ga | V | Others | Al |
| each | total |
| 3104 | ≤0.8 | ≤0.6 | 0.05-0.25 | 0.8-1.4 | 0.8-1.3 | ≤0.1 | ≤0.25 | ≤0.05 | ≤0.05 | 0.05 | 0.15 | Other |
Mechanical property and Process property
| Mechanical property | Process Property |
| Tensile Strength Rm | Yield Strength Rp0.2 | Post Baked Elongation A50mm/% | Post Baked Yield Strength (205℃/10min 400°F/10min) | Earing /% |
| ≥293MPa | 270-305MPa | ≥4.0 | 255-288MPa | ≤4 |
1.5 Oscillation and Telescoping
The oscillation shall not be more than 2mm,and telescoping no more than 5mm.
1.6 Edge camber
The edge camber shall not be more than 1mm maximum in 1000mm on the strip
1.7 Flatness
The gap between the strip and the flat surface should less than 6mm, the amount of wave in one meter length should no more than 3.
1.8 Surface Roughness:Ra:0.30~0.60 μm.
2. Appearance quality
The surface should be clean, even texture. Defects which may affect the material processing are forbidden, such as serious scratches, speckles, corrosions, oil stains, air entrapments, holes, peeling, inclusions, metal and nonmetal inclusions, black streaks or black lines.
2.2. The trimmed coil must be without cracks,clean cutting edge
2.3. The coils should be tight and even on the edges ,no splice
Can supply
aluminum coil for beverage cans
aluminum coil for aluminum cans
aluminum can body stock
aluminum alloy 3004 h19 for can stock
body stock coil
coil stock price
coil aluminium
Application
Can Body and body stock
beverage cans ,can stock
Beverage can
beer can, juice
Surface Lubrication
| Post Lube | Post Lube Control Amount |
| Henkel DTI PL-A | 250±125mg/m2/side 25.0±12.5mg/ft2/side |
Application:
Features:
Aluminum plate for Al - 5182 Mg of antirust aluminum, 5182 performance similar to 5 how a02 aluminum plate, but because of a little higher than 5 how a02 magnesium content, and added a small amount of silicon, so the weldability is better than 5 how a02, 5182 aluminum plate with gas welding and argon arc welding, spot welding and welding seam welding performance is very good, other performance has no big difference.
5182 belong to Al - Mg alloy, using a wide range, especially construction cannot leave the alloy, is the most promising alloy. Good corrosion resistance, good weldability, cold workability is good, and with moderate intensity. 5052 main alloy elements for magnesium, has good forming performance, corrosion resistance, weldability and medium strength, used to make airplane oil tank, oil pipe, as well as the transportation vehicles, ships, sheet metal parts, instrument, lamps stent and rivet, metal products, electrical enclosure, etc.
Packing Photos
Product Tags:
|
|
405MM Aluminum Coil Stock For Can Body A3104 Temper H19 Images
|